تفاصيل الوثيقة نوع الوثيقة : مقال في مجلة دورية  عنوان الوثيقة : Optical properties of LiF:Mg,Cu,P nanorods Optical properties of LiF:Mg,Cu,P nanorods   الموضوع : فيزياء  لغة الوثيقة : الانجليزية  المستخلص : Nanorods of LiF:Mg,Cu,P synthesised by the chemical co-precipitation technique have been investigated for their optical properties. Photoluminescence (PL) emission and excitation spectra and UV-visible absorption spectrum have been investigated in this paper. PL emission spectrum shows a wide emission band located at the range 350 nm-450 nm along with emerging of a sharp intense band at 376 nm. Normally, a broad emission band is observed in the bulk (micro/single crystal) material of LiF:Mg,Cu,P which is due to Cu+ transition. The nanorods have sizes approximately 50 nm in diameter and several hundreds nm in length. The sharp band at 376 nm may be attributed to quantum confinement. Moreover, the result obtained from the UV-visible absorption measurement is consistent with the PL result. It shows a broad absorption band contains a small sharp one at around 373 nm. These remarkable results might be useful for some applications such as high power lasers.  ردمد : 1752-8933  اسم الدورية : International Journal of Nano and Biomaterials  المجلد : 2  العدد : 1  سنة النشر : 1430 هـ 2009 م  نوع المقالة : مقالة علمية  تاريخ الاضافة على الموقع : Wednesday, December 21, 2011  الباحثون اسم الباحث (عربي) اسم الباحث (انجليزي) نوع الباحث المرتبة العلمية البريد الالكتروني نعمان صلاح Salah, Numan باحث دكتوراه nsalah@kau.edu.sa سامي حبيب Habib, Sami باحث دكتوراه sami_habib@hotmail.com ذيشان حسين خان Khan, Zishan H باحث دكتوراه zishan_hk@yahoo.co.in أحمد عبدالله الغامدي Al-Ghamdi, Ahmad A باحث دكتوراه AGAMDI@kau.edu.sa الملفات اسم الملف النوع الوصف  31709.pdf pdf Abstract الرجوع إلى صفحة الأبحاث